60Si2Mn is a silico-manganese spring steel with high strength, elasticity and hardenability. It is used for flat springs, coil springs and heat-resistant springs with a working temperature of 250 ℃ or less.
60Si2Mn is a high-strength, high-silicon, and high-manganese alloy used for making various springs and wear-resistant parts. Learn about its chemical composition, physical and mechanical properties, industries and applications, and machining processes.
60Si2Mn is a steel grade with chemical composition of 0.56-0.64% C, 1.50-2.00% Si, 0.60-0.90% Mn, and others. It has mechanical properties of yield strength 233 MPa, tensile strength 957 MPa, elongation 33%, and modulus of elasticity 213 GPa.
GB 60SI2MN is a high quality alloy spring steel with good hardenability and mechanical properties. Otai Special Steel offers round bar, flat bar, plate, hexagonal bar and square bar in various sizes and tolerances.
60Si2Mn is a structure steel grade with 0.56-0.64% silicon and 1.50-2.00% manganese. It has high tensile strength, yield strength, elongation and hardness, and can be produced in various forms and dimensions.
60Si2Mn steel coil is a widely used silicon-manganese spring steel, which has high hardenability, good thermal processing performance, stable process performance, good comprehensive mechanical properties, decarburization resistance, high fatigue strength and anti-shock performance and so on. JIS SUP6 / DIN 1.0909 / GB 60Si2Mn steel coil composition and more information as below.
60Si2Mn density of 7.85g / cm3. 60Si2Mn is widely used silicon manganese spring steel, strength, elasticity and hardenability than 55Si2Mn slightly higher. Suitable for railway vehicles, automobile tractor industry to produce a larger load of flat springs or wire diameter of 30mm below the coil spring.
Learn about the chemical composition, mechanical, physical and environmental properties of grade 60Si2Mn steel, a type of structural steel and alloy steel. See the specifications, dimensions, heat treatment, surface conditions and service of this steel grade.
The manganese in 60Si2Mn can improve the hardenability. Due to its high silicon content, its strength, hardenability, and tempering resistance are higher than those of carbon spring steel. However, due to its high silicon content, it has a high likelihood of surface decarburization and low cold deformation plasticity.
Non-Magnetic Steel in the 60Si2Mn Special Alloy grade; Steels of Blade for Steam Turbine in the 60Si2Mn Special Alloy grade; Involving various fields like aviation, aerospace, shipbuilding, petrochemical, nuclear power, electronics, turbine, high-speed rail, marine engineering, pressure vessel and machinery manufacturing, etc., SteelGr has ...